3 weeks ago, one of my customers tells me he wants us to make SS201 barn door hardware. He is a door hardware importer and wholesaler. Price is important to their market, quality is second, he always said. As a sliding barn door hardware manufacturer, we will love to develop a new product. After searching on the internet, there is no SS201 Barn Door Hardware Online . Som ni vet är den största skillnaden mellan 201 och 304 anti-korrosionsprestanda . Vi producerar också skjutdörrhårdvara, så SS201 är inte lämpad för vårt behov . är det något annat material kan uppfylla vår begäran? Sedan hittade jag det nya klass rostfritt stål - SS204CU . Det är ett billigt alternativ till typ 304.
Vad är 204CU
204Cu is also called S20430, is the United States developed many years ago. By adding 3% copper to modified type 201, a new alloy was developed that bridges the cost/property gap between the 200 and 300 series stainless steel. This new alloy, known as Type 204Cu, had a lower cost than Type 304 due to approximately 6% lower nickel content. It hade bättre formbarhet än 201 och typ 304 på grund av kopparstillägget som sänkte arbetshärdningshastigheten . korrosionsmotstånd var som typ 304 på grund av en noggrann balans mellan legeringselement som inkluderar krom och nickel .}
Kemisk sammansättning (%)
AisI | C | Si | Mn | P | S | Ni | Cr | Cu | N |
204CU | 0.15 | 1.00 | 6.50-9.00 | 0.060 | 0.03 | 1.50-3.50 | 15.50-17.50 | 2.00-4.00 | 0.05-0.25 |
304 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 8.00-10.50 | 18.00-20.00 | 0.10 |
Tabellen visar det olika elementinnehållet mellan 204CU och 304. jämfört med 304, nickelinnehåll minskat med 5 ~ 6 procentenheter, och lägger till ett litet antal Cu -element . och det har bra rost och korrosionsmotstånd, liknande prestanda till 304. Det kan tillgodose de dagliga behoven i den allmänna användningen av strukturell stål. Element .
Kol (C): Järn legerat med kol för att tillverka stål och har effekten av att öka hårdhetens hårdhet och styrka .
Krom (CR): Krom tillsätts till stål för att öka resistensen mot oxidation . Detta motstånd ökar när mer krom läggs till .
Nickel (Ni): Nickel tillsätts i stora mängder, över cirka 8%. Högkrom rostfria stål för att bilda den viktigaste klassen av korrosion och värmemotstånd .}
Koppar (Cu): Koppar tillsätts till några legeringar för att producera nederbördshärdande egenskaper . och förbättra korrosionsbeständighet, särskilt i havsvattenmiljöer och svavelsyra .}
Kostnadsjämförelse
Vårt mål är att försöka hitta ett billigt råmaterial . En experimentproduktionsutvärdering visade att typ 204CU var kapabel att bearbetas till kallt ritad tråd på liknande sätt som typ 304. och finishtrådskostnaden för typ 204cu var lägre på grund av Alloy's 6% Lower Nickel -innehåll {{5} it Can Saving $ 75 {nästan 9} {{nästan 6}) En tredjedel av de 304 priserna . och den har en liknande anti-rostförmåga . Anta att materialkostnaden är 30% av den totala kostnaden, det kan spara 10% på det sista priset.
Pris är viktigt, även kvaliteten . Låt oss se de mekaniska egenskaperna och korrosionsbeständigheten .
Mekaniska egenskaper
Stainless steel product is made of 204Cu is possible, it has similar production cost. Another program was to establish the formability of Type 204Cu in comparison to Type 304. Type 204Cu was developed to bridge the gap between the 200 and 300 series of alloys. Type 204Cu has lower alloy cost than Type 304 due to lower nickel but similar processing cost due to a similar work härdningshastighet . också, typ 204CU har bättre formbarhet än typ 304 trots högre glödgad styrka .
204Cu have good performance in formability, even better than 304. Several hundred parts were cold-formed for each alloy, and parts were examined for cracks on the formed head. The fewer the percent cracked parts, the better the formability. An experiment showed Type 201 Modified had the worst formability with the highest percentage of cracked heads. Type 204Cu had a much lower percent of cracked parts than the forming quality version of Type 304 (2% vs. 37%). These results were unexpected and demonstrated that Type 204Cu had bridged the formability gap between the 200 and 300 series of austenitic stainless alloys.
Korrosionsmotstånd
On the door hardware industry, the anti-rust property is main different between 201 and 304. Salt spray tests were performed of wire for the three alloys by ASTM B117, 201, 204Cu and 304. The salt spray environment was 5% NaCl at a 95F temperature in an enclosed cabinet for 96 hours. Visual examination of the wire revealed that rust only occurred on the Modifierad typ 201 -tråd . Således hade typ 204CU liknande saltspraybeständighet som typ 304.
Beside this salt spray tests, another study below. Study of Leaching of iron, Chromium, Nickel and Copper in different food products when cooked in stainless steel coupons/cookware. Results are tabulated for eight food simulants and actual food media for Fe, Cr, Ni and Cu. The value of leached elements obtained through Atomic absorption spectrometry after keeping coupons of size 50mmx70mm and cookware 100mm diameter(made by the deep drawn process) in 150 ml of simulant for boiling ~30 minutes. The solution was concentrated on a water bath for removal of water content in simulant solution /food. The concentrate was made into ash by digesting in a heated muffle furnace. Ash solutions were prepared for each Simulant genom att lösa respektive aska i 2% salpetersyralösning . Den aska -lösningen användes sedan för atomabsorptionsspektrometri .
Slutsats: Lakningsvärdena för krom och nickel är mycket låga i alla fall<0.1 ppm. It was observed that there were no surface corrosion spot/rust marks in the tested coupons/cookware and no measurable weight loss when compared before and after the experiment.
204Cu exhibits general atmospheric corrosion resistance in non-coastal and non-toxic environments like Type 304. 204Cu has unique corrosion resistance to H2SO4, and the corrosion resistance of HC1 and HNO3 is better than 304. But the high-temperature oxidation resistance is worse than that of 304. It is not suitable to be used in the Oxidationsmiljö med hög temperatur (större än eller lika med 400 ° C) . Vår produkt är inre dörrhårdvara, så det är inte ett problem .
Ansökningar
Som ett effektivt kostnadsalternativ till typ 201/304 hittar 204CU ett brett utbud av applikationer . De framstående områdena är:
1. Catering- och livsmedelsprocess: Djupt ritade köksutrustning, redskap, köksredskap, industriutrustning, kolvar, mjölkburkar, is- och vattendispensrar, vattenfilter, inhemska och kommersiella kylskåp yttre kroppsdelar .}
2. Konsumentvaror: Sänkor, brödrostar, mikrovågsugnar yttre kroppsdelar, bakugnar, termovaror, tvättmaskiner yttre kroppsdelar, mobilfodral /delar .
3. Arkitektur-, byggnads- och konstruktionshandstänger för en trappa, hissar, rulltrappor, inre paneler, dörrfönster, termiska fönsteravstånd, eldbox .
4. Transport (Automotive) Automotive slangklämmor, säkerhetsbälte förankringar, lastbil och busram .
5. Branschtobaksbearbetningsindustrin, avloppsreningsverkstrukturer, bulkfast materialhanteringsutrustning, speciella fästelement på grund av en kombination av hög styrka och god formbarhet för dator, pol-linjehårdvara i telefonpoler i telefonkommunikationsindustrin, transportband i livsmedelsförädlingsenheter .}
Det finns mycket hårdvara är tillverkad av 204CU . som rostfritt ståltrådar, rör, skruvar . flänsar och gångjärn . 204 Cu Sliding Barn Door Hardware kommer att ses på marknaden .}
Slutsats
Compare with 304, 204Cu have a better price and suitable quality. Considering that China is a country with a relative lack of nickel resources, and the price of international nickel is too high, and most of the domestic use requirements are not very high. With the increasing familiarity of the market, the application scope of 204Cu will be more and wider, and the future may be replaced by 304 in some Områden . Jag håller helt med om att .
Så vi kan se AISI204 -handtag eller ladugårdshårdvara i framtiden . och om du vill vara den första katten, vill försöka producera lite för att testa marknaden . kontakta oss utan att tveka . är vi en tillverkare och letar efter en ny möjlighet.}}
Hänvisning
1. Utveckling av typ 204 Cu rostfritt, en låg kostnadsalternativ till typ 304
2. Rostfritt stål Grad J 204CU
http: // www . Gual . es/img/imatges _ cms/dokument/193Jindal204Cu . pdf
3. 204CU rostfritt stål UNS20430
https: // www . ulbrich . com/resurser/strip-datasheets/204cu-rostfritt stål-uns20430/
4. SS 204CU, typ 204CU, UNS S20430, AISI 204CU, produkter tillgängliga WNR 1.4597
PS: Det här är min första långa artikel . för jag är nu en far . min baby flicka är 3 månader gammal . Jag kommer att stressa mer för att göra henne stolt .. Därför börjar jag mitt skrivande nu .}